CELANEX4309AR
CELANEX庐 PBTPBT-I-GF30CharacteristicsRegional availabilityProcessingInjection MouldingDelivery formPelletsSpecial characteristicsHydrolysis resistantProduct TextCelanex 4309AR is a 30% glass reinforced PBT with enhanced resistance to hydrolysis, alkaline environments and salt water spray.Product information
ValueTest NormResin IdentificationPBT-I-GF30*** 1043Part Marking Code>PBT-I-GF30<*** 11469Rheological properties
ValueUnitTest NormMelt mass-flow rate13g/10min*** 1133Melt mass-flow rate, Temperature265掳CMelt mass-flow rate, Load5kgMoulding shrinkage range, parallel0.3 - 0.6%*** 294-4, 2577Moulding shrinkage range, normal1.4 - 1.6%*** 294-4, 2577Mechanical properties
ValueUnitTest NormTensile modulus8100MPa*** 527-1/-2Tensile stress at break, 5mm/min100MPa*** 527-1/-2Tensile strain at break, 5mm/min3%*** 527-1/-2Flexural modulus7600MPa*** 178Flexural strength150MPa*** 178Charpy impact strength, 23掳C45kJ/m虏*** 179/1eUCharpy impact strength, -30掳C50kJ/m虏*** 179/1eUCharpy notched impact strength, 23掳C10kJ/m虏*** 179/1eACharpy notched impact strength, -30掳C8.7kJ/m虏*** 179/1eAIzod notched impact strength, 23掳C9kJ/m虏*** 180/1AIzod impact strength, 23掳C40kJ/m虏*** 180/1UHardness, Rockwell, M-scale62*** 2039-2Poisson&锛�39;s ratio0.34[C][C]: CalculatedThermal properties
ValueUnitTest NormMelting temperature, 10掳C/min220掳C*** 11357-1/-3Temperature of deflection under load, 1.8 MPa191掳C*** 75-1/-2Temperature of deflection under load, 0.45 MPa217掳C*** 75-1/-2Coefficient of linear thermal expansion (CLTE), parallel23E-6/K*** 11359-1/-2Coefficient of linear thermal expansion (CLTE), normal95E-6/K*** 11359-1/-2Flammability
ValueUnitTest NormBurning Behav. at thickness hHBclassIEC 60695-11-10Thickness tested0.8mmIEC 60695-11-10Physical/Other properties
ValueUnitTest NormDensity1440kg/m鲁*** 1183Injection
ValueUnitDrying RecommendedyesDrying Temperature120掳CDrying Time, Dehumidified Dryer4hProcessing Moisture Content鈮�0.02%Melt Temperature Optimum250掳CMin. melt temperature240掳CMax. melt temperature260掳CScrew tangential speed0.1 - 0.3m/sMold Temperature Optimum80掳CMin. mould temperature60掳CMax. mould temperature130掳CEjection temperature185掳CAdditional informationProcessing NotesPre-Drying
4 Hrs. at 250F, <0.02% moisture
Automotive
OEMAdditional InformationHondaValidated for Strut sensor by HGT