CELANEX 5206HG
CELANEX庐 PBT(PET+PBT)-GF15CharacteristicsRegional availabilityNorth America
Europe
Asia Pacific
South and Central America
Near East/Africa
Global
Product information
ValueTest NormResin Identification(PBT+PET)-GF15*** 1043Part Marking Code>(PBT+PET)-GF15<*** 11469Rheological properties
ValueUnitTest NormMoulding shrinkage range, parallel0.4 - 0.6%*** 294-4, 2577Mechanical properties
ValueUnitTest NormTensile modulus6400MPa*** 527-1/-2Tensile stress at break, 5mm/min95MPa*** 527-1/-2Tensile strain at break, 5mm/min1.8%*** 527-1/-2Flexural modulus6300MPa*** 178Flexural strength140MPa*** 178Charpy notched impact strength, 23掳C4.7kJ/m虏*** 179/1eAIzod notched impact strength, 23掳C4.5kJ/m虏*** 180/1APoisson&锛�39;s ratio0.35[C][C]: CalculatedThermal properties
ValueUnitTest NormMelting temperature, 10掳C/min250掳C*** 11357-1/-3Temperature of deflection under load, 1.8 MPa180掳C*** 75-1/-2Temperature of deflection under load, 0.45 MPa220掳C*** 75-1/-2Flammability
ValueUnitTest NormBurning Behav. at thickness hHBclassIEC 60695-11-10Thickness tested0.8mmIEC 60695-11-10Physical/Other properties
ValueUnitTest NormDensity1450kg/m鲁*** 1183Injection
ValueUnitDrying RecommendedyesDrying Temperature135掳CDrying Time, Dehumidified Dryer4hProcessing Moisture Content鈮�0.01%Melt Temperature Optimum290掳CMin. melt temperature270掳CMax. melt temperature300掳CScrew tangential speed0.1 - 0.3m/sMold Temperature Optimum130掳CMin. mould temperature120掳CMax. mould temperature140掳CAdditional informationInjection moldingProcessing
Rear Temperature 480-500 (250-260) deg F (deg C)
Center Temperature 490-510 (255-265) deg F (deg C)
Front Temperature 500-540 (260-270) deg F (deg C)
Nozzle Temperature 510-520 (265-275) deg F (deg C)
Melt Temperature 520-570 (270-300) deg F (deg C)
Mold Temperature 250-275 (120-135) deg F (deg C)
Back Pressure 0-25 psi
Screw Speed 50-75 rpm
Injection Speed Medium/Fast
Injection speed, injection pressure and holding pressure have to be optimized to the individual article geometry. To avoid material degradation during processing low back pressure and minimum screw speed have to be used. Overheating of the material has to be avoided. Up to 25% clean and dry regrind may be used.
Pre-Drying
To avoid hydrolytic degradation during processing, Impet resins have to be dried to a moisture level equal to or less than 0.01%. Drying should be done in a dehumidifying hopper dryer capable of dewpoints <-40掳F (-40掳C) at 275掳F (135掳C) for 4 hours.
Storage
For subsequent storage of the material in the dryer until processed (<= 60 h) it is necessary to lower the temperature to 100掳 C.