CELANEX 5600-2
CELANEX庐 PBT(PBT+PET)-GF55CharacteristicsRegional availabilityProcessingInjection MouldingProduct TextCELANEX庐 5600-2 is 55% fiber glass reinforced polyester with excellent dimensional stability and mechanical properties.Product information
ValueTest NormResin Identification(PBT+PET)-GF55*** 1043Part Marking Code>(PBT+PET)-GF55<*** 11469Rheological properties
ValueUnitTest NormMelt mass-flow rate7.7g/10min*** 1133Melt mass-flow rate, Temperature265掳CMelt mass-flow rate, Load2.16kgMoulding shrinkage range, parallel0.2 - 0.3%*** 294-4, 2577Moulding shrinkage range, normal0.3 - 0.5%*** 294-4, 2577Mechanical properties
ValueUnitTest NormTensile modulus20600MPa*** 527-1/-2Tensile stress at break, 5mm/min172MPa*** 527-1/-2Tensile strain at break, 5mm/min1.4%*** 527-1/-2Flexural modulus20500MPa*** 178Flexural strength270MPa*** 178Charpy notched impact strength, 23掳C11kJ/m虏*** 179/1eACharpy notched impact strength, -30掳C11kJ/m虏*** 179/1eAPoisson&锛�39;s ratio0.33[C][C]: CalculatedThermal properties
ValueUnitTest NormTemperature of deflection under load, 1.8 MPa210掳C*** 75-1/-2Coefficient of linear thermal expansion (CLTE), normal, 55-160掳C92E-6/K*** 11359-1/-2Coefficient of linear thermal expansion (CLTE), parallel, 55-160掳C13E-6/K*** 11359-1/-2Physical/Other properties
ValueUnitTest NormDensity1820kg/m鲁*** 1183Injection
ValueUnitDrying RecommendedyesDrying Temperature120掳CDrying Time, Dehumidified Dryer4hProcessing Moisture Content鈮�0.02%Melt Temperature Optimum265掳CMin. melt temperature255掳CMax. melt temperature275掳CScrew tangential speed0.1 - 0.3m/sMold Temperature Optimum100掳CMin. mould temperature90掳CMax. mould temperature130掳CAdditional informationProcessing NotesPre-Drying
To avoid hydrolytic degradation during processing, CELANEX resins have to be dried to a moisture level equal to or less than 0.02%. Drying should be done in a dehumidifying hopper dryer capable of dewpoints <-40掳F (-40掳C) at 250掳F (121掳C) for 4 hours.
Storage
For subsequent storage of the material in the dryer until processed (<= 60 h) it is necessary to lower the temperature to 100掳 C.
Automotive
OEMStandardAdditional InformationGeneral MotorsGMW18161P-PBT+PET-GF55Black;ED3002