CELANEX庐 2104UV North America Europe Asia Pacific South and Central America Near East/Africa Global Product information Rheological properties Mechanical properties Thermal properties Electrical properties Physical/Other properties Injection Pre-Drying Diagrams
ProcessingInjection MouldingDelivery formPelletsAdditivesRelease agentSpecial characteristicsHigh impact or impact modified, U.V. stabilised or stable to weather, ColourableProduct TextCelanex 2104UV is an unreinforced, impact modified, UV stabilized PBT designed for outdoor agricultural, industrial and automotive applications. Celanex 2104UV is suitable for injection molding applications.
To avoid hydrolytic degradation during processing, CELANEX resins have to be dried to a moisture level equal to or less than 0.02%. Drying should be done in a dehumidifying hopper dryer capable of dewpoints <-40掳F (-40掳C) at 250掳F (121掳C) for 4 hours.
Storage
For subsequent storage of the material in the dryer until processed (<= 60 h) it is necessary to lower the temperature to 100掳 C.
Disclaimer
Privacy Policy
Sitemap
Copyright 漏 2025 All rights reserved.
CELANEX庐 2104UV
CELANEX庐 PBTPBT-ICharacteristicsRegional availabilityNorth America
Europe
Asia Pacific
South and Central America
Near East/Africa
Global
Product information
ValueTest NormResin IdentificationPBT*** 1043Part Marking Code>PBT<*** 11469Rheological properties
ValueUnitTest NormMelt mass-flow rate3g/10min*** 1133Melt mass-flow rate, Temperature250掳CMelt mass-flow rate, Load2.16kgMoulding shrinkage range, parallel2.2 - 3.3%*** 294-4, 2577Moulding shrinkage range, normal2.2 - 3.3%*** 294-4, 2577Mechanical properties
ValueUnitTest NormTensile modulus2100MPa*** 527-1/-2Tensile stress at yield, 50mm/min46MPa*** 527-1/-2Tensile strain at yield, 50mm/min10%*** 527-1/-2Nominal strain at break>50%*** 527-1/-2Flexural modulus2080MPa*** 178Flexural strength63MPa*** 178Charpy impact strength, 23掳CNkJ/m虏*** 179/1eUCharpy impact strength, -30掳CNkJ/m虏*** 179/1eUCharpy notched impact strength, 23掳C15kJ/m虏*** 179/1eACharpy notched impact strength, -30掳C6.9kJ/m虏*** 179/1eAIzod notched impact strength, 23掳C3.7kJ/m虏*** 180/1AIzod impact strength, 23掳C123kJ/m虏*** 180/1UPoisson&锛�39;s ratio0.4[C][C]: CalculatedThermal properties
ValueUnitTest NormMelting temperature, 10掳C/min225掳C*** 11357-1/-3Temperature of deflection under load, 0.45 MPa130掳C*** 75-1/-2Electrical properties
ValueUnitTest NormRelative permittivity, 100Hz4IEC 62631-2-1Relative permittivity, 1MHz3.5IEC 62631-2-1Dissipation factor, 100Hz70E-4IEC 62631-2-1Dissipation factor, 1MHz200E-4IEC 62631-2-1Volume resistivity>1E13Ohm.mIEC 62631-3-1Surface resistivity>1E15OhmIEC 62631-3-2Electric strength23kV/mmIEC 60243-1Physical/Other properties
ValueUnitTest NormDensity1310kg/m鲁*** 1183Injection
ValueUnitDrying RecommendedyesDrying Temperature120掳CDrying Time, Dehumidified Dryer4hProcessing Moisture Content鈮�0.04%Melt Temperature Optimum250掳CMin. melt temperature240掳CMax. melt temperature260掳CScrew tangential speed0.1 - 0.3m/sMold Temperature Optimum80掳CMin. mould temperature60掳CMax. mould temperature130掳CAdditional informationProcessing NotesPre-Drying
To avoid hydrolytic degradation during processing, CELANEX resins have to be dried to a moisture level equal to or less than 0.02%. Drying should be done in a dehumidifying hopper dryer capable of dewpoints <-40掳F (-40掳C) at 250掳F (121掳C) for 4 hours.
Storage
For subsequent storage of the material in the dryer until processed (<= 60 h) it is necessary to lower the temperature to 100掳 C.
Diagrams
Disclaimer
Privacy Policy
Sitemap
Copyright 漏 2025 All rights reserved.CELANEX庐 2104UV
North America
Europe
Asia Pacific
South and Central America
Near East/Africa
Global
Product information
ValueTest NormResin IdentificationPBT*** 1043Part Marking Code>PBT<*** 11469Rheological properties
ValueUnitTest NormMelt mass-flow rate3g/10min*** 1133Melt mass-flow rate, Temperature250掳CMelt mass-flow rate, Load2.16kgMoulding shrinkage range, parallel2.2 - 3.3%*** 294-4, 2577Moulding shrinkage range, normal2.2 - 3.3%*** 294-4, 2577Mechanical properties
ValueUnitTest NormTensile modulus2100MPa*** 527-1/-2Tensile stress at yield, 50mm/min46MPa*** 527-1/-2Tensile strain at yield, 50mm/min10%*** 527-1/-2Nominal strain at break>50%*** 527-1/-2Flexural modulus2080MPa*** 178Flexural strength63MPa*** 178Charpy impact strength, 23掳CNkJ/m虏*** 179/1eUCharpy impact strength, -30掳CNkJ/m虏*** 179/1eUCharpy notched impact strength, 23掳C15kJ/m虏*** 179/1eACharpy notched impact strength, -30掳C6.9kJ/m虏*** 179/1eAIzod notched impact strength, 23掳C3.7kJ/m虏*** 180/1AIzod impact strength, 23掳C123kJ/m虏*** 180/1UPoisson&锛�39;s ratio0.4[C][C]: CalculatedThermal properties
ValueUnitTest NormMelting temperature, 10掳C/min225掳C*** 11357-1/-3Temperature of deflection under load, 0.45 MPa130掳C*** 75-1/-2Electrical properties
ValueUnitTest NormRelative permittivity, 100Hz4IEC 62631-2-1Relative permittivity, 1MHz3.5IEC 62631-2-1Dissipation factor, 100Hz70E-4IEC 62631-2-1Dissipation factor, 1MHz200E-4IEC 62631-2-1Volume resistivity>1E13Ohm.mIEC 62631-3-1Surface resistivity>1E15OhmIEC 62631-3-2Electric strength23kV/mmIEC 60243-1Physical/Other properties
ValueUnitTest NormDensity1310kg/m鲁*** 1183Injection
ValueUnitDrying RecommendedyesDrying Temperature120掳CDrying Time, Dehumidified Dryer4hProcessing Moisture Content鈮�0.04%Melt Temperature Optimum250掳CMin. melt temperature240掳CMax. melt temperature260掳CScrew tangential speed0.1 - 0.3m/sMold Temperature Optimum80掳CMin. mould temperature60掳CMax. mould temperature130掳CAdditional informationProcessing NotesPre-Drying
To avoid hydrolytic degradation during processing, CELANEX resins have to be dried to a moisture level equal to or less than 0.02%. Drying should be done in a dehumidifying hopper dryer capable of dewpoints <-40掳F (-40掳C) at 250掳F (121掳C) for 4 hours.
Storage
For subsequent storage of the material in the dryer until processed (<= 60 h) it is necessary to lower the temperature to 100掳 C.
Diagrams
Disclaimer
Privacy Policy
Sitemap
Copyright 漏 2025 All rights reserved.CELANEX庐 2104UV
North America
Europe
Asia Pacific
South and Central America
Near East/Africa
Global
Product information
ValueTest NormResin IdentificationPBT*** 1043Part Marking Code>PBT<*** 11469Rheological properties
ValueUnitTest NormMelt mass-flow rate3g/10min*** 1133Melt mass-flow rate, Temperature250掳CMelt mass-flow rate, Load2.16kgMoulding shrinkage range, parallel2.2 - 3.3%*** 294-4, 2577Moulding shrinkage range, normal2.2 - 3.3%*** 294-4, 2577Mechanical properties
ValueUnitTest NormTensile modulus2100MPa*** 527-1/-2Tensile stress at yield, 50mm/min46MPa*** 527-1/-2Tensile strain at yield, 50mm/min10%*** 527-1/-2Nominal strain at break>50%*** 527-1/-2Flexural modulus2080MPa*** 178Flexural strength63MPa*** 178Charpy impact strength, 23掳CNkJ/m虏*** 179/1eUCharpy impact strength, -30掳CNkJ/m虏*** 179/1eUCharpy notched impact strength, 23掳C15kJ/m虏*** 179/1eACharpy notched impact strength, -30掳C6.9kJ/m虏*** 179/1eAIzod notched impact strength, 23掳C3.7kJ/m虏*** 180/1AIzod impact strength, 23掳C123kJ/m虏*** 180/1UPoisson&锛�39;s ratio0.4[C][C]: CalculatedThermal properties
ValueUnitTest NormMelting temperature, 10掳C/min225掳C*** 11357-1/-3Temperature of deflection under load, 0.45 MPa130掳C*** 75-1/-2Electrical properties
ValueUnitTest NormRelative permittivity, 100Hz4IEC 62631-2-1Relative permittivity, 1MHz3.5IEC 62631-2-1Dissipation factor, 100Hz70E-4IEC 62631-2-1Dissipation factor, 1MHz200E-4IEC 62631-2-1Volume resistivity>1E13Ohm.mIEC 62631-3-1Surface resistivity>1E15OhmIEC 62631-3-2Electric strength23kV/mmIEC 60243-1Physical/Other properties
ValueUnitTest NormDensity1310kg/m鲁*** 1183Injection
ValueUnitDrying RecommendedyesDrying Temperature120掳CDrying Time, Dehumidified Dryer4hProcessing Moisture Content鈮�0.04%Melt Temperature Optimum250掳CMin. melt temperature240掳CMax. melt temperature260掳CScrew tangential speed0.1 - 0.3m/sMold Temperature Optimum80掳CMin. mould temperature60掳CMax. mould temperature130掳CAdditional informationProcessing NotesPre-Drying
To avoid hydrolytic degradation during processing, CELANEX resins have to be dried to a moisture level equal to or less than 0.02%. Drying should be done in a dehumidifying hopper dryer capable of dewpoints <-40掳F (-40掳C) at 250掳F (121掳C) for 4 hours.
Storage
For subsequent storage of the material in the dryer until processed (<= 60 h) it is necessary to lower the temperature to 100掳 C.
Diagrams
Disclaimer
Privacy Policy
Sitemap
Copyright 漏 2025 All rights reserved.CELANEX庐 2104UV
North America
Europe
Asia Pacific
South and Central America
Near East/Africa
Global
Product information
ValueTest NormResin IdentificationPBT*** 1043Part Marking Code>PBT<*** 11469Rheological properties
ValueUnitTest NormMelt mass-flow rate3g/10min*** 1133Melt mass-flow rate, Temperature250掳CMelt mass-flow rate, Load2.16kgMoulding shrinkage range, parallel2.2 - 3.3%*** 294-4, 2577Moulding shrinkage range, normal2.2 - 3.3%*** 294-4, 2577Mechanical properties
ValueUnitTest NormTensile modulus2100MPa*** 527-1/-2Tensile stress at yield, 50mm/min46MPa*** 527-1/-2Tensile strain at yield, 50mm/min10%*** 527-1/-2Nominal strain at break>50%*** 527-1/-2Flexural modulus2080MPa*** 178Flexural strength63MPa*** 178Charpy impact strength, 23掳CNkJ/m虏*** 179/1eUCharpy impact strength, -30掳CNkJ/m虏*** 179/1eUCharpy notched impact strength, 23掳C15kJ/m虏*** 179/1eACharpy notched impact strength, -30掳C6.9kJ/m虏*** 179/1eAIzod notched impact strength, 23掳C3.7kJ/m虏*** 180/1AIzod impact strength, 23掳C123kJ/m虏*** 180/1UPoisson&锛�39;s ratio0.4[C][C]: CalculatedThermal properties
ValueUnitTest NormMelting temperature, 10掳C/min225掳C*** 11357-1/-3Temperature of deflection under load, 0.45 MPa130掳C*** 75-1/-2Electrical properties
ValueUnitTest NormRelative permittivity, 100Hz4IEC 62631-2-1Relative permittivity, 1MHz3.5IEC 62631-2-1Dissipation factor, 100Hz70E-4IEC 62631-2-1Dissipation factor, 1MHz200E-4IEC 62631-2-1Volume resistivity>1E13Ohm.mIEC 62631-3-1Surface resistivity>1E15OhmIEC 62631-3-2Electric strength23kV/mmIEC 60243-1Physical/Other properties
ValueUnitTest NormDensity1310kg/m鲁*** 1183Injection
ValueUnitDrying RecommendedyesDrying Temperature120掳CDrying Time, Dehumidified Dryer4hProcessing Moisture Content鈮�0.04%Melt Temperature Optimum250掳CMin. melt temperature240掳CMax. melt temperature260掳CScrew tangential speed0.1 - 0.3m/sMold Temperature Optimum80掳CMin. mould temperature60掳CMax. mould temperature130掳CAdditional informationProcessing NotesPre-Drying
To avoid hydrolytic degradation during processing, CELANEX resins have to be dried to a moisture level equal to or less than 0.02%. Drying should be done in a dehumidifying hopper dryer capable of dewpoints <-40掳F (-40掳C) at 250掳F (121掳C) for 4 hours.
Storage
For subsequent storage of the material in the dryer until processed (<= 60 h) it is necessary to lower the temperature to 100掳 C.
Diagrams
Disclaimer
Privacy Policy
Sitemap
Copyright 漏 2025 All rights reserved.CELANEX庐 2104UV
North America
Europe
Asia Pacific
South and Central America
Near East/Africa
Global
Product information
ValueTest NormResin IdentificationPBT*** 1043Part Marking Code>PBT<*** 11469Rheological properties
ValueUnitTest NormMelt mass-flow rate3g/10min*** 1133Melt mass-flow rate, Temperature250掳CMelt mass-flow rate, Load2.16kgMoulding shrinkage range, parallel2.2 - 3.3%*** 294-4, 2577Moulding shrinkage range, normal2.2 - 3.3%*** 294-4, 2577Mechanical properties
ValueUnitTest NormTensile modulus2100MPa*** 527-1/-2Tensile stress at yield, 50mm/min46MPa*** 527-1/-2Tensile strain at yield, 50mm/min10%*** 527-1/-2Nominal strain at break>50%*** 527-1/-2Flexural modulus2080MPa*** 178Flexural strength63MPa*** 178Charpy impact strength, 23掳CNkJ/m虏*** 179/1eUCharpy impact strength, -30掳CNkJ/m虏*** 179/1eUCharpy notched impact strength, 23掳C15kJ/m虏*** 179/1eACharpy notched impact strength, -30掳C6.9kJ/m虏*** 179/1eAIzod notched impact strength, 23掳C3.7kJ/m虏*** 180/1AIzod impact strength, 23掳C123kJ/m虏*** 180/1UPoisson&锛�39;s ratio0.4[C][C]: CalculatedThermal properties
ValueUnitTest NormMelting temperature, 10掳C/min225掳C*** 11357-1/-3Temperature of deflection under load, 0.45 MPa130掳C*** 75-1/-2Electrical properties
ValueUnitTest NormRelative permittivity, 100Hz4IEC 62631-2-1Relative permittivity, 1MHz3.5IEC 62631-2-1Dissipation factor, 100Hz70E-4IEC 62631-2-1Dissipation factor, 1MHz200E-4IEC 62631-2-1Volume resistivity>1E13Ohm.mIEC 62631-3-1Surface resistivity>1E15OhmIEC 62631-3-2Electric strength23kV/mmIEC 60243-1Physical/Other properties
ValueUnitTest NormDensity1310kg/m鲁*** 1183Injection
ValueUnitDrying RecommendedyesDrying Temperature120掳CDrying Time, Dehumidified Dryer4hProcessing Moisture Content鈮�0.04%Melt Temperature Optimum250掳CMin. melt temperature240掳CMax. melt temperature260掳CScrew tangential speed0.1 - 0.3m/sMold Temperature Optimum80掳CMin. mould temperature60掳CMax. mould temperature130掳CAdditional informationProcessing NotesPre-Drying
To avoid hydrolytic degradation during processing, CELANEX resins have to be dried to a moisture level equal to or less than 0.02%. Drying should be done in a dehumidifying hopper dryer capable of dewpoints <-40掳F (-40掳C) at 250掳F (121掳C) for 4 hours.
Storage
For subsequent storage of the material in the dryer until processed (<= 60 h) it is necessary to lower the temperature to 100掳 C.
Diagrams
Disclaimer
Privacy Policy
Sitemap
Copyright 漏 2025 All rights reserved.CELANEX庐 2104UV
North America
Europe
Asia Pacific
South and Central America
Near East/Africa
Global
Product information
ValueTest NormResin IdentificationPBT*** 1043Part Marking Code>PBT<*** 11469Rheological properties
ValueUnitTest NormMelt mass-flow rate3g/10min*** 1133Melt mass-flow rate, Temperature250掳CMelt mass-flow rate, Load2.16kgMoulding shrinkage range, parallel2.2 - 3.3%*** 294-4, 2577Moulding shrinkage range, normal2.2 - 3.3%*** 294-4, 2577Mechanical properties
ValueUnitTest NormTensile modulus2100MPa*** 527-1/-2Tensile stress at yield, 50mm/min46MPa*** 527-1/-2Tensile strain at yield, 50mm/min10%*** 527-1/-2Nominal strain at break>50%*** 527-1/-2Flexural modulus2080MPa*** 178Flexural strength63MPa*** 178Charpy impact strength, 23掳CNkJ/m虏*** 179/1eUCharpy impact strength, -30掳CNkJ/m虏*** 179/1eUCharpy notched impact strength, 23掳C15kJ/m虏*** 179/1eACharpy notched impact strength, -30掳C6.9kJ/m虏*** 179/1eAIzod notched impact strength, 23掳C3.7kJ/m虏*** 180/1AIzod impact strength, 23掳C123kJ/m虏*** 180/1UPoisson&锛�39;s ratio0.4[C][C]: CalculatedThermal properties
ValueUnitTest NormMelting temperature, 10掳C/min225掳C*** 11357-1/-3Temperature of deflection under load, 0.45 MPa130掳C*** 75-1/-2Electrical properties
ValueUnitTest NormRelative permittivity, 100Hz4IEC 62631-2-1Relative permittivity, 1MHz3.5IEC 62631-2-1Dissipation factor, 100Hz70E-4IEC 62631-2-1Dissipation factor, 1MHz200E-4IEC 62631-2-1Volume resistivity>1E13Ohm.mIEC 62631-3-1Surface resistivity>1E15OhmIEC 62631-3-2Electric strength23kV/mmIEC 60243-1Physical/Other properties
ValueUnitTest NormDensity1310kg/m鲁*** 1183Injection
ValueUnitDrying RecommendedyesDrying Temperature120掳CDrying Time, Dehumidified Dryer4hProcessing Moisture Content鈮�0.04%Melt Temperature Optimum250掳CMin. melt temperature240掳CMax. melt temperature260掳CScrew tangential speed0.1 - 0.3m/sMold Temperature Optimum80掳CMin. mould temperature60掳CMax. mould temperature130掳CAdditional informationProcessing NotesPre-Drying
To avoid hydrolytic degradation during processing, CELANEX resins have to be dried to a moisture level equal to or less than 0.02%. Drying should be done in a dehumidifying hopper dryer capable of dewpoints <-40掳F (-40掳C) at 250掳F (121掳C) for 4 hours.
Storage
For subsequent storage of the material in the dryer until processed (<= 60 h) it is necessary to lower the temperature to 100掳 C.