CELANEX 2405MT
CELANEX庐 PBT
PBT
Characteristics
Processing
Injection Moulding
Delivery form
Pellets
Additives
Lubricants, Release agent, Low wear / Low friction
Product Text
Celanex 2405MT is an unfilled, tribologically-modified, medium flow PBT grade for injection molding processing.
Celanex 2405MT is a special grade developed for medical industry applications and complies with:
CFR 21 (177.1660) of the Food and Drug Administration (FDA) and is listed in the Drug Master File (DMF 10047 (US) / 10033 (EU)) and the Device Master File (MAF 443 (US) / 1078 (EU))
the corresponding EU and national registry regulatory requirements
biocompatibility in tests corresponding to USP 23 Class VI/*** 10993
low residual monomers
no animal products
Product information
Value
Test Norm
Resin Identification
PBT
*** 1043
Part Marking Code
>PBT<
*** 11469
Rheological properties
Value
Unit
Test Norm
Melt volume-flow rate
20
cm鲁/10min
*** 1133
Temperature
250
掳C
Load
2.16
kg
Moulding shrinkage, parallel
1.8
%
*** 294-4, 2577
Moulding shrinkage range, parallel
1.5 - 2
%
*** 294-4, 2577
Moulding shrinkage, normal
1.8
%
*** 294-4, 2577
Moulding shrinkage range, normal
1.5 - 2
%
*** 294-4, 2577
Mechanical properties
Value
Unit
Test Norm
Tensile modulus
2600
MPa
*** 527-1/-2
Tensile stress at yield, 50mm/min
60
MPa
*** 527-1/-2
Tensile strain at yield, 50mm/min
4
%
*** 527-1/-2
Tensile stress at 50% strain
30
MPa
*** 527-1/-2
Nominal strain at break
>50
%
*** 527-1/-2
Flexural modulus
2500
MPa
*** 178
Flexural strength
80
MPa
*** 178
Charpy impact strength, 23掳C
N
kJ/m虏
*** 179/1eU
Charpy impact strength, -30掳C
190
kJ/m虏
*** 179/1eU
Charpy notched impact strength, 23掳C
5
kJ/m虏
*** 179/1eA
Charpy notched impact strength, -30掳C
5
kJ/m虏
*** 179/1eA
Izod notched impact strength, 23掳C
5
kJ/m虏
*** 180/1A
Poisson&锛�39;s ratio
0.38[C]
[C]: Calculated
Thermal properties
Value
Unit
Test Norm
Melting temperature, 10掳C/min
225
掳C
*** 11357-1/-3
Glass transition temperature, 10掳C/min
60
掳C
*** 11357-1/-3
Temperature of deflection under load, 1.8 MPa
55
掳C
*** 75-1/-2
Temperature of deflection under load, 0.45 MPa
150
掳C
*** 75-1/-2
Vicat softening temperature, 50掳C/h 50N
190
掳C
*** 306
Coefficient of linear thermal expansion (CLTE), parallel
110
E-6/K
*** 11359-1/-2
Flammability
Value
Unit
Test Norm
Burning Behav. at thickness h
HB
class
IEC 60695-11-10
Thickness tested
0.8
mm
IEC 60695-11-10
Oxygen index
20
%
*** 4589-1/-2
Electrical properties
Value
Unit
Test Norm
Relative permittivity, 100Hz
4
IEC 62631-2-1
Relative permittivity, 1MHz
3.5
IEC 62631-2-1
Dissipation factor, 100Hz
14
E-4
IEC 62631-2-1
Dissipation factor, 1MHz
220
E-4
IEC 62631-2-1
Volume resistivity
1E13
Ohm.m
IEC 62631-3-1
Surface resistivity
1E15
Ohm
IEC 62631-3-2
Electric strength
23
kV/mm
IEC 60243-1
Comparative tracking index
600
IEC 60112
Physical/Other properties
Value
Unit
Test Norm
Density
1310
kg/m鲁
*** 1183
Injection
Value
Unit
Drying Recommended
yes
Drying Temperature
140
掳C
Drying Time, Dehumidified Dryer
4 - 6
h
Processing Moisture Content
鈮�0.01
%
Melt Temperature Optimum
250
掳C
Min. melt temperature
240
掳C
Max. melt temperature
260
掳C
Screw tangential speed
0.1 - 0.3
m/s
Mold Temperature Optimum
80
掳C
Min. mould temperature
60
掳C
Max. mould temperature
130
掳C
Ejection temperature
188
掳C
Additional information
Injection molding
To minimize the volatile content in the final product, dry the resin to 鈮�0.01% water content. In injection molding, use the lowest possible melt temperature (recommended 240 掳C) and shortest feasible residence time (recommended 2-3 minutes). Store the parts in a ventilated, clean area before use. If assistance is needed please contact your Celanese account representative.
These recommendations are based on internal Celanese testing. For drying and injection molding conditions outside the above parameters, customer must test for and verify suitably low volatiles emissions on molded articles to confirm the final product is suitably pure for its intended use.
Processing Notes